Iron Vanadyòm Alloy gratis echantiyon
| Klas | V | sizo | al | C | S | P | Kòm | Taks | Mn |
|---|---|---|---|---|---|---|---|---|---|
| FeV75C{{1}.1 | 70–85 | 0.8 | 2 | 0.1 | 0.05 | 0.05 | 0.05 | 0.1 | 0.4 |
| FeV75C{{1}.15 | 70–85 | 1 | 2.5 | 0.15 | 0.1 | 0.1 | 0.05 | 0.1 | 0.6 |
| FeV5{{1}C0.4 | 48–60 | 1.8 | 0.2 | 0.4 | 0.02 | 0.07 | 0.01 | 0.2 | 2.7 |
| FeV5{{1}C0.5 | 48–60 | 2 | 0.3 | 0.5 | 0.02 | 0.07 | 0.01 | 0.2 | 4 |
| FeV5{{1}C0.6 | 48–60 | 2 | 0.3 | 0.6 | 0.03 | 0.07 | 0.02 | 0.2 | 5 |
| Fev5{{1}C0.3 | >50 | 2 | 2.5 | 0.3 | 0.1 | 0.1 | 0.05 | 0.2 | 0.2 |
| Fev5{{1}C0.75 | >50 | 2 | 2.5 | 0.75 | 0.1 | 0.1 | 0.05 | 0.2 | 0.2 |
| FeV4{{1}C0.5 | 35–48 | 2 | 0.5 | 0.5 | 0.05 | 0.08 | 0.03 | 0.4 | 2 |
| FeV4{{1}C0.75 | 35–48 | 2 | 0.5 | 0.75 | 0.05 | 0.08 | 0.03 | 0.4 | 4 |
| Fev40C1 | 35–48 | 2 | 0.5 | 1 | 0.05 | 0.1 | 0.03 | 0.4 | 6 |
| FeV 50% | FeV 80% |
| V: 50% Min. | V: 80.0% Min. |
| C: 0.10% Max | C: 0.10% Max |
| S: 0.05% Max | S: 0.05% Max |
| P: 0.10% Max | P: 0.10% Max |
| Si: 1.5% Max | Si: 1.5% Max |
| Al: 1.5% Max | Al: 1.5% Max |
FeVanadium nan faktori endistri
Vanadyòm Iron Alloy nan faktori endistri
Ferovanadiummetòd fusion
Metòd elèktrosilikotèmal: Flake vanadyòm pentoksid itilize 75% ferosilicon ak yon ti kantite aliminyòm kòm ajan rediksyon, epi li rafine nan yon founo elektrik alkalin ak de etap nan rediksyon ak raffinage pou jwenn pwodwi ki kalifye.
Pandan peryòd rediksyon an, yo mete tout ajan rediksyon yo nan yon sèl gwo founo dife ak {{0}}% nan total pentoksid vanadyòm flake nan fou elektrik la, epi rediksyon tèmik Silisyòm fèt anba gwo salop oksid kalsyòm. Lè V2O5 nan salop la se mwens pase 0.35%, salop la lage (yo rele salop mèg, ki ka jete oswa itilize kòm materyèl bilding) epi li antre nan peryòd raffinage.
Nan moman sa a, yo ajoute pentoksid vanadyòm flake ak lacho pou retire depase Silisyòm, aliminyòm, elatriye nan likid alyaj la. Yon fwa konpozisyon ferroalloy la rive nan nivo ki nesesè yo, ferroalloy la ka egzeyate salop. Salop la lage nan etap la pita nan raffinage yo rele salop rich (ki gen V2O5 jiska 8 ~ 12%) epi yo pral retounen nan gwo founo dife a pou itilize ankò lè chaje kòmanse nan gwo fou a.
Se likid alyaj la jeneralman jete nan lengote silendrik, epi yo jwenn pwodwi a fini apre refwadisman, demoulding, kraze ak retire salop. Metòd sa a jeneralman itilize pou fusion ferrovanadium ki gen 40 ~ 60% vanadyòm. Pousantaj rekiperasyon vanadyòm ka rive nan 98%. Rafine chak tòn ferrovanadium konsome apeprè 1,600 èdtan kilowat elektrisite.
Vanadyòm Ferroalloys nan faktori endistri
Klas 75-80 Ferro Vanadium Factory
Alyaj fè ak vanadyòm Founisè
Baj popilè: vanadyòm ferroalloys 50 80, Lachin vanadyòm ferroalloys 50 80 manifaktirè, founisè, faktori